In Situ and Real-Time Studies, via Synchrotron X-ray Scattering, of the Orientational Order of Cellulose Nanocrystals during Solution Shearing. Academic Article uri icon

Overview

abstract

  • In this manuscript, we report on the ordering of the cellulose nanocrystals (CNCs) as they experience shear forces during the casting process. To achieve these measurements, in situ and in real time, we used synchrotron-based grazing incidence wide-angle X-ray scattering (GIWAX). We believe that the GIWAX technique, although not commonly used to probe these types of phenomena, can open new avenues to gain deeper insights into film formation processes and surface-driven phenomena. In particular, we investigated the influence of solution concentration, shear-cast velocity, and drying temperature on the ordering of cellulose nanocrystals (CNCs) using GIWAXS. The films were prepared from aqueous suspensions of cellulose nanocrystals at two concentration values (7 and 9 wt %). As the films were cast, the X-ray beam was focused on a fixed position and GIWAXS patterns were recorded at regular time intervals. Structural characterization of the dry films was carried out via polarized optical microscopy and scanning electron microscopy. In addition, a rheological study of the CNC suspensions was performed. Our results show that the morphology of the CNC films was significantly influenced by shear velocity, concentration of the precursor suspension, and evaporation temperature. In contrast, we observed that the orientation parameter of the films was not significantly affected. The scattering intensity of the peak (200) was analyzed as a function of time, following a sigmoidal profile, hence indicating short- and long-range interactions within the anisotropic domains as they reached their final orientation state. A model capable of describing the resulting film morphologies is also proposed. The results and analysis presented in this manuscript provide new insights into the controlled alignment of cellulose nanocrystals under shear. This controlled alignment has significant implications in the development of advanced coatings and films currently used in a myriad of applications, such as catalysis, optics, electronics, and biomedicine.

publication date

  • April 23, 2018

Identity

Scopus Document Identifier

  • 85046639939

Digital Object Identifier (DOI)

  • 10.1021/acs.langmuir.7b04403

PubMed ID

  • 29641208

Additional Document Info

volume

  • 34

issue

  • 18